Epoxy-Modified Silicone Resin of Iota E-30
HomeHome > Products > Epoxy Resin for Electronics > Epoxy-Modified Silicone Resin of Iota E-30
Epoxy-Modified Silicone Resin of Iota E-30

Epoxy-Modified Silicone Resin of Iota E-30

Product name:Epoxy-modified silicone resin IOTA H-30 Description and application This product has a relatively good resi
Basic Info
Model NO. IOTA H-30
Transport Package Iron Drum
Specification 25kg or 200kg
Trademark IOTA
Origin China
HS Code 39100000
Production Capacity 100ton/Month
Product Description

Product name:Epoxy-modified silicone resin IOTA H-30
Description and application
This product has a relatively good resistance to high and low temperature, hydrophobic moisture resistance and good electrical insulation properties, arc resistance corona performance. Its weather resistance and chemical stability, corrosion resistance is also very good.
This product is widely used as high-temperature anti-corrosion coatings (≥500ºC) , can be completely cured two-component at room temperature, the property will be better after roast solidification. It could also be used as H grade insulating material.

Technical index

 

Epoxy-Modified Silicone Resin of Iota E-30

How to use?
A: two components solid at room temperature. Could be used with 650 polyamide or T-31. The 650 adding amount is about 10~15% of the resin total amount. The T-31 adding amount is about 5~7%of the resin total amount.
B: Oven curing at high temperature, it fully solidified after 1.5 hour at 180~200ºC.

Notes
The diluting solvent used in this product should not contains water, pyridine sulfur-containing compounds and impurities, otherwise it will affect the resin film adhesion, dry and other properties.
There will be a lot of xylene and other flammable, toxic solvents evaporate during the production process, we should pay special attention to strengthening the field of ventilation, attention to fire safety, strict cut off the source of fire. The operator should pay attention to labor protection.
The processing equipment, utensils must be clean during the production process. To prevent dust,foreign matter and water.
The products such as acid,alkali,salt of organic acid amine compounds has Accelerate the solidification effectiveness for this product, and will influence the heat resistance and electrical properties. So, this product should be isolated with those products when storing.Storage This product should be stored in ventilated, cool, dry place to prevent direct sunlight exposure; to prevent serious pollution of acid, lye, and should be cut off from sources of ignition away from heat, the product storage period is six months.Packing 200kg white iron drum